Ibanga Nokubunjwa Kwekhemikhali (%)
Ibanga | C | Mn | P≤ | S≤ | Si | Cr | Mo |
T11 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 0.50-1.00 | 1.00-1.50 |
T12 | 0.05-0.15 | 0.30-0.61 | 0.025 | 0.025 | ≤0.50 | 0.80-1.25 | 0.44-0.65 |
T13 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | ≤0.50 | 1.90-2.60 | 0.87-1.13 |
Izakhiwo zikaMechanical(MPa):
Ibanga | I-Tensile Point | Yield Point |
T11 | ≥415 | ≥205 |
T12 | ≥415 | ≥220 |
T13 | ≥415 | ≥205 |
Ukuhlola Okungaphandle Kobubanzi
Ukuhlola Ukuqina Kwezindonga
Qeda Ukuhlola
Ukuhlola Ukuqondile
Ukuhlolwa kwe-UT
Ukuhlola Ukubukeka
Amashubhu ensimbi angenamthungo e-ASTM A213 akhiqizwa ngokudonswa okubandayo noma ngokugoqwa okushisayo, njengoba kucacisiwe.Ibanga le-TP347HFG lizophela ngokubanda.Ukwelashwa kokushisa kufanele kwenziwe ngokwehlukana futhi ngaphezu kokufudumeza ukwakheka okushisayo.I-ferritic alloy nezinsimbi ezingenasici ze-ferritic zizoshiswa kabusha.Ngakolunye uhlangothi, amashubhu ensimbi engagqwali ye-austenitic azonikezwa esimweni sokwelashwa ngokushisa.Ngaphandle kwalokho, ngokushesha ngemva kokwakhiwa okushisayo, kuyilapho izinga lokushisa lamashubhu lingekho ngaphansi kwezinga lokushisa elincane lesisombululo, amashubhu angase acinywe ngamanye emanzini noma apholiswe ngokushesha ngezinye izindlela.
I-JIS G3441Alloy Seamless Steel amashubhu
I-ASTM A519 Alloy ipayipi yensimbi engenamthungo
I-ASTM A335 Alloy steel piepe engenamthungo